Search found 447 matches
- Tue Jan 12, 2016 11:30 am
- Forum: Ski/Snowboard Design and Layup
- Topic: glass-carbon rescue
- Replies: 17
- Views: 11490
- Tue Jan 12, 2016 5:13 am
- Forum: Ski/Snowboard Design and Layup
- Topic: glass-carbon rescue
- Replies: 17
- Views: 11490
- Sun Jan 10, 2016 8:17 am
- Forum: Ski/Snowboard Design and Layup
- Topic: glass-carbon rescue
- Replies: 17
- Views: 11490
- Sat Jan 09, 2016 10:55 am
- Forum: Ski/Snowboard Design and Layup
- Topic: glass-carbon rescue
- Replies: 17
- Views: 11490
Lol, my denglish seems to lead to the wrong direction ;) Normally i use just 1 layer of 750 triax glas. Now i like to use just 1 layer of 450 triax carbon. In my opinion it would make the ski stiffer with same core dimensions. So ... how much to shave off the core to get with the carbon same flex as...
- Sat Jan 09, 2016 2:13 am
- Forum: Equipment and Tools (e.g., ski press, core profiler, etc)
- Topic: Splitboard inside edge grinding
- Replies: 25
- Views: 19263
- Sat Jan 09, 2016 2:06 am
- Forum: Ski/Snowboard Design and Layup
- Topic: glass-carbon rescue
- Replies: 17
- Views: 11490
The binding screws are no problem, the 6mm was mid shovel! Problem with my machine did create just problems in the thinner parts of the core, not the center. I will reshape the core so the original profile is back, the whole core will be then about 0.5 - 1.0 mm thinner (i did build this core profile...
- Fri Jan 08, 2016 3:25 pm
- Forum: Equipment and Tools (e.g., ski press, core profiler, etc)
- Topic: Splitboard inside edge grinding
- Replies: 25
- Views: 19263
- Fri Jan 08, 2016 8:41 am
- Forum: Ski/Snowboard Design and Layup
- Topic: glass-carbon rescue
- Replies: 17
- Views: 11490
Too thin is up to 0.5/0.8 mm mid shovel (e.g 6 -> 5.5) on a superwide ski. Dont have exact measurements on hand, the core sits somewhere in my workshop since last winter. Is there no thumb rule for glas -> carbon (like 15% less core)? Would be cool to have a starting point. From then its experimenti...
- Fri Jan 08, 2016 4:59 am
- Forum: Ski/Snowboard Design and Layup
- Topic: glass-carbon rescue
- Replies: 17
- Views: 11490
- Fri Jan 08, 2016 3:06 am
- Forum: Ski/Snowboard Design and Layup
- Topic: glass-carbon rescue
- Replies: 17
- Views: 11490
glass-carbon rescue
Have a f.u. core from last season which my machine made too thin on some places. Its ash wood. Do you guys think its possible to use carbon (450g triax) instead of glas (750g triax) to compensate for the missing thickness? Or lets ask like that ... how much can be a core thinner when using this carb...
- Fri Jan 08, 2016 2:15 am
- Forum: Equipment and Tools (e.g., ski press, core profiler, etc)
- Topic: Splitboard inside edge grinding
- Replies: 25
- Views: 19263
- Sun Jan 03, 2016 2:01 pm
- Forum: Journals: Log Your Ski Building Progress
- Topic: H-H log
- Replies: 13
- Views: 11911
- Sun Jan 03, 2016 11:32 am
- Forum: Equipment and Tools (e.g., ski press, core profiler, etc)
- Topic: Wooden bottom mold
- Replies: 21
- Views: 13968
Thats true because its more easy to work with (router).
Motoman used another wood and was not so happy ... http://www.skibuilders.com/phpBB2/viewtopic.php?t=4991
Motoman used another wood and was not so happy ... http://www.skibuilders.com/phpBB2/viewtopic.php?t=4991
- Thu Dec 31, 2015 3:38 am
- Forum: Aprés Ski Building
- Topic: treefrogs new shop is finally under way!
- Replies: 27
- Views: 29352
- Sat Dec 26, 2015 4:06 am
- Forum: Journals: Log Your Ski Building Progress
- Topic: HB (Hansen Boards)
- Replies: 224
- Views: 128339