Yesterday has made one more snowboard for my wife =)
284/254/284 152 sm.
The rocker of 10/350 mm. full twintip.
The core - a pine.
(Forgive me for photos - phone)
top
base
rocker tip
rocker tail
core profile
[/img]
my best girlfriend
Moderators: Head Monkey, kelvin, bigKam, skidesmond, chrismp
my best girlfriend
From R with l
Murchonn
Murchonn
-
- Posts: 1354
- Joined: Mon Sep 17, 2007 7:37 pm
Looks great!
So much going on. Hopefully you can understand my questions.
The core profile? Real thick under bindings. How is the flex? Is it a consistent flex, or does it only flex in the center and on the tips?
Is that abs in the center? Looks like you removed wood and added abs? For weight?
What are the diagonal lines on the base? Looks like glass fibers weaved through the edges?
Very cool. Thanks so much for sharing.
So much going on. Hopefully you can understand my questions.
The core profile? Real thick under bindings. How is the flex? Is it a consistent flex, or does it only flex in the center and on the tips?
Is that abs in the center? Looks like you removed wood and added abs? For weight?
What are the diagonal lines on the base? Looks like glass fibers weaved through the edges?
Very cool. Thanks so much for sharing.
- MontuckyMadman
- Posts: 2395
- Joined: Fri Jun 20, 2008 9:41 pm
-
- Posts: 2337
- Joined: Tue Apr 07, 2009 3:26 pm
- Location: Western Mass, USA
- Contact:
Last snowboard was very rigid.
The idea was to make it snowboard more softly) has for this purpose planned such core. After to it the profile the core has been set it has appeared very soft =)
Has decided to make inserts and to strengthen glass)
As it has appeared - in vain)))
Again rigid it has turned out) though more softly than the first)
This all experiments!))) I not snowboarder)
Today we go to mountains - there all we will test) basically powder)))
Let's shoot on GoPro - we will look that will turn out)))
MontuckyMadman - about the wife knew that so you will write!))) thanks!!!
About a drawing - I will write later
Thank you
The idea was to make it snowboard more softly) has for this purpose planned such core. After to it the profile the core has been set it has appeared very soft =)
Has decided to make inserts and to strengthen glass)
As it has appeared - in vain)))
Again rigid it has turned out) though more softly than the first)
This all experiments!))) I not snowboarder)
Today we go to mountains - there all we will test) basically powder)))
Let's shoot on GoPro - we will look that will turn out)))
MontuckyMadman - about the wife knew that so you will write!))) thanks!!!
About a drawing - I will write later
Thank you
From R with l
Murchonn
Murchonn