Your biax flax 4.7uni cf and a 12 mm waist should be plenty stiff. Be sure to put your cf next to the core. Tip from a buddy in big time snowboard biz.
Fighting gravity on a daily basis
www.Whiteroomcustomskis.com
www.Whiteroomcustomskis.com
-
- Posts: 175
- Joined: Mon Oct 11, 2010 11:06 pm
- Contact:
I just made a splitboard with 3.7ounce 45/45 carbon, and 4 ounce uni carbon. I used close to my usual core thickness, and the thing came out stiff as hell. I rode it today, way to stiff. unmanageable torsional stiffness. carved groomers like a laser, but in the waist deep backcountry it was hard turning and nose dove on anything that was not super steep. my carbon experiment is bound to be retired on the wall.
I am looking very forward to trying some flax also.
9 ounce unicarbon would be way to stiff(just my opinion)
Question........I plan to build this carbon splitboard again. thinning my core will make a world of difference in the tip to tail flex, but how much of an effect will it have on the torsional flex(softening it)?
Sorry for the thread hijack!
I am looking very forward to trying some flax also.
9 ounce unicarbon would be way to stiff(just my opinion)
Question........I plan to build this carbon splitboard again. thinning my core will make a world of difference in the tip to tail flex, but how much of an effect will it have on the torsional flex(softening it)?
Sorry for the thread hijack!
No idea on the core , but if all was you did was change to biax glass and maybe thin the core some, you'd probably be in the ball park.
Fighting gravity on a daily basis
www.Whiteroomcustomskis.com
www.Whiteroomcustomskis.com
- MontuckyMadman
- Posts: 2395
- Joined: Fri Jun 20, 2008 9:41 pm
I clearly messed upped in my novice composites calculations. I don't think of my experimenting as waste really. Just part of the hobby.
When was the last time I saw a post with anthing that you made sucsessfully or unsucessfully for that matter MM?
All I see from you is enough criticism and smart remarks to make me think you hardly build skis, and are probably just a bored man with a beer gut trying to feel imoprtant.
You have not really contributed anything worth while to this site in a long time.
Maybe instead of mounting my splitboard on the shop wall, I'll mount your head. It will make for a good conversation piece.
When was the last time I saw a post with anthing that you made sucsessfully or unsucessfully for that matter MM?
All I see from you is enough criticism and smart remarks to make me think you hardly build skis, and are probably just a bored man with a beer gut trying to feel imoprtant.
You have not really contributed anything worth while to this site in a long time.
Maybe instead of mounting my splitboard on the shop wall, I'll mount your head. It will make for a good conversation piece.
-
- Posts: 175
- Joined: Mon Oct 11, 2010 11:06 pm
- Contact:
If you wanna have a less stiff ski without sacrificing strength you can make the ud bottom laminate lighter than the one above. Makes quite a big difference in stiffness. And I might help you out with the composite calculations to get exactly the same flex as one of your fg boards. If you're interested send me a pm...
Cheers Reto
Cheers Reto
-
- Posts: 2337
- Joined: Tue Apr 07, 2009 3:26 pm
- Location: Western Mass, USA
- Contact:
All good info guys thanks! Vin, I saw a video (somewhere on the internet,I watch too much of that stuff :-) ) where the CF was on the inside covered over in another material. It wasn't FG or Flax, some other plasticy or nylon type material. It "mellowed" out the CF so it was less likely to snap and made it a little bit more pliable.
The 9 oz CF I used in my sample is way to stiff. It's tricky that CF it's so thin pliable until you lay it up and then it become rock hard.
I'll pick up some uni-CF in the 4-5 oz range.
The 9 oz CF I used in my sample is way to stiff. It's tricky that CF it's so thin pliable until you lay it up and then it become rock hard.
I'll pick up some uni-CF in the 4-5 oz range.
Last edited by skidesmond on Mon Dec 16, 2013 9:38 am, edited 1 time in total.
-
- Posts: 175
- Joined: Mon Oct 11, 2010 11:06 pm
- Contact:
I wouldn't go too light with the fabric. You might weaken the ski because face wrinkling (or was it buckling? I always mess up the words in english...) Will occur more likely. That said I don't know what "too light" is. But probably a mix between a thinner core and lighter fabric might be the best solution.
Fighting gravity on a daily basis
www.Whiteroomcustomskis.com
www.Whiteroomcustomskis.com
- MontuckyMadman
- Posts: 2395
- Joined: Fri Jun 20, 2008 9:41 pm
Hey D you should mount it to my head when you come by my shop and converse about custom skis.
I was merely being sarcastic as it happens to all of us.
You should see my wall of failures and I have to stop drinking.
I dont have time to upload pics and I help people everyday on here but I'm starting to think its a waste of time as no one listens at all.
Come by and I can make you something.
www.northsideskis.com
I was merely being sarcastic as it happens to all of us.
You should see my wall of failures and I have to stop drinking.
I dont have time to upload pics and I help people everyday on here but I'm starting to think its a waste of time as no one listens at all.
Come by and I can make you something.
www.northsideskis.com
sammer wrote: I'm still a tang on top guy.
-
- Posts: 175
- Joined: Mon Oct 11, 2010 11:06 pm
- Contact: